Graphite material has the advantages of high temperature resistance, corrosion resistance and good thermal conductivity, and plays an important role in the copper casting industry, for example, graphite die used for oxygen-free copper tube of upward pulling process.
Our original coating technology makes graphite die outstanding in hardness, wear resistance, and oxidation resistance, thus prolonging the service life of graphite die by 3-5 times.
In addition, our company has accumulated many years of experience in machining, making the size of graphite die more precise, which can be controlled within ±0.02mm.
Copper pipe mold material technical parameters as following:
Materials | LTHG-S |
Bulk Density g/cm3 | 1.85 |
Electrical Resistivity uΩ·m | 8-9 |
Flexural Strength MPa | ≥55 |
Compressive Strength MPa | ≥95 |
Ash content % | ≤0.03 |
Graininess | 8-10 microns |
Graphite material has the advantages of high temperature resistance, corrosion resistance and good thermal conductivity, and plays an important role in the copper casting industry, for example, graphite die used for oxygen-free copper tube of upward pulling process.
Our original coating technology makes graphite die outstanding in hardness, wear resistance, and oxidation resistance, thus prolonging the service life of graphite die by 3-5 times.
In addition, our company has accumulated many years of experience in machining, making the size of graphite die more precise, which can be controlled within ±0.02mm.
Copper pipe mold material technical parameters as following:
Materials | LTHG-S |
Bulk Density g/cm3 | 1.85 |
Electrical Resistivity uΩ·m | 8-9 |
Flexural Strength MPa | ≥55 |
Compressive Strength MPa | ≥95 |
Ash content % | ≤0.03 |
Graininess | 8-10 microns |